Fatigue behavior of zirconia under different loading conditions

详细信息    查看全文

• 作者：Moustafa N. Aboushelib ; DDS ; MSc ; PhD^a ; ^{bluemarline_1@yahoo.com" class="auth_mail" title="E-mail the corresponding author} ; ^{moustafaaboushelib@gmail.com" class="auth_mail" title="E-mail the corresponding author} ; Hang Wang ; BDS ; DDS ; PhD^b ; Cornelis J. Kleverlaan ; PhD^c ; Albert J. Feilzer ; DDS ; PhD^c
• 关键词：Zirconia ; Fatigue ; Static ; Dynamic ; Cyclic loading ; Residual strength
• 刊名：Dental Materials
• 出版年：2016
• 出版时间：July 2016
• 年：2016
• 卷：32
• 期：7
• 页码：915-920
• 全文大小：1833 K

文摘

To investigate the influence of surface damage on the fatigue behavior of zirconia under two different loading conditions.

Materials and methods

One hundred twenty zirconia bar-shaped received either airborne particle abrasion using 50 μm or 120 μm alumina particles while polished specimens served as control. The specimens were subjected to two fatigue regimes: dynamic fatigue (1,000,000 cycles, 1 hz and 0.5 s contact time) or static fatigue (a constant load applied for 5000 s) under water using the staircase application of the load. The flexure strength after fatigue (dynamic fatigue strength) was compared to the initial flexure strength of the tested specimens (α = 0.05). The critical crack shape and size of fractured specimens was examined using scanning electron microscopy.

Results

Compared to the initial flexure strength of the tested specimens, dynamic fatigue strength was 86.3% for the polished specimens, 73.4% for 50 μm particle abrasion, and 42.3% for 120 μm particle abrasion while the static fatigue strength was 85.9%, 78.5%, and 51.5% respectively. Significant statistical differences (F = 223.679, P < 0.001) were found between different surface treatments but not between dynamic and static fatigue strengths for the same type of surface treatment.

Conclusions

The dynamic and static fatigue strengths of zirconia are significantly influenced by type of surface damage.

Clinical Implications

Within the limitations of this study, surface damage have great influence on fatigue behavior of zirconia.