Point defect formation and annihilation in silica glass by heat-treatment: Role of water and stress
详细信息    查看全文
文摘
It was discovered that E′ centers were created by heat-treatment when silica glass contains water and has residual stress. Silica glass samples were heat-treated at 1000 °C for various lengths of time in 355 torr (47 000 Pa) water vapor pressure and dry nitrogen gas atmospheres. The electron paramagnetic resonance (EPR) signal of E′ centers increased initially with heat-treatment time in both atmospheres but then decreased afterwards in the wet atmosphere. It is known that water molecules eliminate paramagnetic defects, such as E′ centers and non-bridging oxygen hole centers (NBOHCs) by reacting with these defects in the glass, transforming them to non-paramagnetic species such as mdash"" border=0>Si–OH or mdash"" border=0>Si–H. The present study indicates that water molecules are also capable of initially creating paramagnetic defects in the glass structure by breaking the silica network structure in the presence of stress. The present observation may be relevant to mechanical strength reduction of silica glasses, which is commonly observed in the presence of water and stress.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700