Phase formation in Al₂O₃-C refractories with Al addition

详细信息    查看全文

• 作者：C. Atzenhofer^a ; ^{christina.atzenhofer@unileoben.ac.at} ; S. Gschiel^b ; H. Harmuth^a
• 关键词：Al2O3-C refractories ; Non-oxides ; Phase formation
• 刊名：Journal of the European Ceramic Society
• 出版年：2017
• 出版时间：April 2017
• 年：2017
• 卷：37
• 期：4
• 页码：1805-1810
• 全文大小：3678 K
• 卷排序：37

文摘

Depending on the recipe and the firing conditions, several non-oxides can be formed in Al2O3-C refractories. In this paper, the effect of the purity of the recipe components on the phase formation in Al2O3-C refractories with Al addition was investigated. Two test series were sintered from 800 °C to 1600 °C under air embedded in coke breeze. One test series was with brown fused alumina, and the other was with tabular alumina. At temperatures of up to 1200 °C the phase formation was the same for both recipes. For temperatures greater than 1400 °C, the impurities of brown fused alumina enhanced the formation of a polytype, while Al4O4C and Al28O21C6N6 were formed in the other series. The findings explain the occurrence of several non-oxides in disequilibrium at the chosen temperatures. The occurrence of Al4C3 was of particular interest due to its low hydration resistance. It was formed at 1200 °C.