A new combined process, ausforming followed by below-Ms austempering, was applied.
The new process significantly refines bainitic structure in a low-carbon steel.
A superfine bainite with lath thickness down to ∼100 nm is obtained.
Bainitic lath thickness decreases as the ausforming temperature decreases.
Ladder-like bainitic morphology is formed at lower ausforming temperatures.