Effects of ausforming temperature on bainite transformation, microstructure and variant selection in nanobainite steel

详细信息    查看全文

• 作者：W. Gong^a ; ^{gong.wu@jaea.go.jp} ; Y. Tomota^b ; Y. Adachi^c ; A.M. Paradowska^d ; ¹ ; J.F. Kelleher^d ; S.Y. Zhang^d
• 关键词：Bainite ; Ausforming ; Phase transformation ; Crystallography ; Neutron diffraction
• 刊名：Acta Materialia
• 出版年：2013
• 出版时间：June, 2013
• 年：2013
• 卷：61
• 期：11
• 页码：4142-4154
• 全文大小：5009 K

文摘

The bainite transformation behavior after plastic deformation of austenite, i.e., ausforming was studied by in situ neutron diffraction and ex situ experiments, and the effects of ausforming temperature was made clear. Ausforming, at a low temperature (573 K) was found to accelerate bainite transformation and produce a characteristic microstructure, whereas at a high temperature (873 K), ausforming had little influence. The reason for the different results stems from the dislocation structure introduced in austenite; planar dislocations remaining on the active slip planes are believed to assist bainite transformation, accompanied by strong variant selection. The variant selection rule that focuses on Shockley partial dislocation was verified from electron backscatter diffraction results.