文摘
The effect of a Zr addition on the precipitation behavior and mechanical properties in Nb-containing alumina-forming austenitic (AFA) stainless steels was investigated using tensile tests, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM) analysis. The TEM observation showed that a Zr addition led to the formation of a (Nb,Zr)(C,N) complex particle, which coarsened the Nb-rich carbonitride. Tensile tests were performed at an elevated temperature (700 掳C), and both the tensile and yield strengths decreased with a Zr addition. This unexpected result of a Zr addition was due to the reduction of the precipitation strengthening by particle coarsening.