Ablation resistance of precursor derived Si-Hf-C-N(O) ceramics
详细信息 查看全文
- 作者：Wasan Awin Eranezhuth ; Soumya Sridar ; Bakthavachalam Kousaalya Adhimoolam1 ; Ravi Kumar ; nvrk@iitm.ac.in" class="auth_mail" title="E-mail the corresponding author
- 关键词：Ablation ; Oxyacetylene flame ; Ceramic foam ; Spark plasma sintering ; Microstructure
- 刊名：Journal of the European Ceramic Society
- 出版年：2016
- 出版时间：November 2016
- 年：2016
- 卷：36
- 期：15
- 页码：3717-3723
- 全文大小：2634 K
文摘
Polymer derived Si-Hf-C-N(O) foams were produced by the pyrolysis of polysilazane containing varying amounts of hafnium tetra n-butoxide. X-ray tomography was used to determine the cell size distribution. The ablation resistance of the foams was studied by subjecting it to different oxyacetylene flame temperatures. After ablation, fragmentation was not observed and the mass ablation rate was found to be minimal for the foams produced from highest vol% of hafnium tetra n-butoxide. The foams remained X-ray amorphous after ablation and the presence of Hf
O and SiO bonds were confirmed using ATR spectroscopy. For comparison, a reasonably dense spark plasma sintered pellet was also ablated and the evolution of monoclinic hafnia was confirmed using X-ray diffraction. The microstructural characterization exhibited three different zones on the ablated surface for sintered sample and the ablation mechanisms were understood using thermodynamic calculations.
O and SiO bonds were confirmed using ATR spectroscopy. For comparison, a reasonably dense spark plasma sintered pellet was also ablated and the evolution of monoclinic hafnia was confirmed using X-ray diffraction. The microstructural characterization exhibited three different zones on the ablated surface for sintered sample and the ablation mechanisms were understood using thermodynamic calculations.