Interfacial fracture of Cu/Ag bimaterials is studied using atomistic simulations.
The fracture patterns are affected by the crystal orientations of the bimaterials.
Atomistic simulations, LEFM, and Griffith theory yield similar fracture toughness.
The scatter in the fracture toughness obtained by atomistic simulations is explained.