C/YIG composites with different carbon content have been prepared by the impregnation-carbonization process.
The percolation phenomenon was observed when the carbon content was between 9 wt% and 13 wt%.
Negative permittivity and negative susceptibility have been obtained in the C/YIG composite with 13 wt% carbon content.