An Eh-pH diagram of Cr–Fe–H2O at 160 °C was produced. Stability of chromite in oxidizing solution is related to its Fe(II) content. A decomposition mechanism for chromite was proposed. Fe, Mg and Al were effectively separated from leachate. Chromium oxide product with about 98% Cr2O3 was prepared.