4.5 wt% Si as-cast sheet with excellent workability was produced by strip casting.
Three 4.5 wt% Si thin sheets were effectively fabricated by warm and cold rolling.
The microstructure and macro-texture of the thin sheets were elucidated.
High magnetic inductions and low iron losses were achieved simultaneously.