Microstructures of Ni-AlN composite coatings prepared by pulse electrodeposition technology

详细信息    查看全文

• 作者：Fafeng Xia^a ; ^{xiaff_npu@126.com} ; Huibin Xu^b ; Chao Liu^c ; ^{msm-liu@126.com} ; Jinwu Wang^d ; Junjie Ding^a ; Chunhua Ma^a
• 关键词：Composite coating ; Pulse electrodeposition ; Characterization ; Compact surface
• 刊名：Applied Surface Science
• 出版年：2013
• 出版时间：15 April, 2013
• 年：2013
• 卷：271
• 期：Complete
• 页码：7-11
• 全文大小：747 K

文摘

Ni-AlN composite coating was fabricated onto the surface of steel substrates by using pulse electrodeposition (PED) technique in this work. The effect of pulse current on the nucleation and growth of grains was investigated using transmission electronic microscopy (TEM), X-ray diffraction (XRD), scanning electronic microscopy (SEM) and atomic force microscopy (AFM), respectively. The results show that the contents of AlN nanoparticles increase with density of pulse current and on-duty ratio of pulse current increasing. Whereas the size of nickel grains decreases with density of pulse current increasing and on-duty ratio of pulse current decreasing. Ni-AlN composite coating consists of crystalline nickel (¡«68 nm) and AlN particles (¡«38 nm). SEM and AFM observations show that the composite coatings obtained by PED showed more compact surfaces and less grain sizes, whereas those obtained by direct current electrodepositing have rougher surfaces and bigger grain sizes.