A novel near-α high temperature Ti alloy was designed and formed by HIP process.
Precipitation of silicide and α2 phase was determined by TEM.
A successive evolution mechanism of the microstructure of HIPed parts was proposed.
Reinforcement mechanism of the novel Ti alloy at high temperature was established.