The fatigue life initially decreased and then increased as the Ta content was increased from 0.027 wt% to 0.18 wt%. The softening rate had declined with Ta content increased and the reduced softening rate was attributed to the increased number of Ta-rich MX particles. The grain size and M23C6 were closely associated with the Ta content. The crack distribution was quite sensitive to the Ta content.