The effects of Cr, Mn and Ni on the formation of ordered ω phases were studied. Mn suppressed the formation of ordered ω phases. ωo and βo phases co-existed in the Cr-containing alloy after annealing. A Ti-Al-Ni ternary phase was identified in Ni-containing TiAl alloy after annealing.