The MMC of 6061 + 4%B4C and 1545 K + 4%B4C were successfully produced by stir casting techniques.
Novel stir casting technique was used - the particles incorporated to the melt by powder master alloy.
Good interface reaction between the matrix and the B4C reinforcements was observed.
The formation of Al3BC and AlB2 phases on the matrix/B4C interface was demonstrated.
1545 K + 4%B4C MMC showed YS = 425 MPa and UTS = 455 MPa and high resistance to intercrystalline corrosion.