A 2D quasi-hexagonal α-Fe2O3 nanoplates/graphene composite was prepared by a one-pot solvothermal process.
Fe2O3/rGO composite shows significantly enhanced electrochemical specific capacitances than either Fe2O3 or rGO, which can reach 1083 F g−1 at 2 A g−1.
Fe2O3/rGO composite retains a capacity of 595 F g−1 at 4 A g−1 after 1000 cycles.