Significant quench sensitivity observed in AA6060 alloy after 30 min natural ageing
Prolonged natural ageing increased hardness and reduced QS.
Low dispersoid density leads to insignificant QS from non-hardening precipitates.
Vacancy supersaturation identified as a contributor to QS.