Fracture behavior of Inconel 601 against carbonate molten salt was studied.
EBSD analysis revealed partial recovery with stress relieving in the sample.
TEM-EDS examination showed de-alloying among grain boundaries.
Stress assisted oxidation was found as the main reason for intergranular failure.