Non-stoichiometric chalcogenide glasses from system As35S65 − xSex were studied. Compositional dependencies of chosen optical parameters were measured. In-situ kinetics of photo-darkening were measured and evaluated using two approaches. Correlation between optical parameters changes and structural changes was observed.