Effect of deep cryogenic treatment on structure-property relationship in an ultrahigh strength Mn-Si-Cr bainite/martensite multiphase rail steel

详细信息    查看全文

• 作者：Kaikai Wang^a ; Zhunli Tan^a ; ^{tzli@bjtu.edu.cn} ; Kaixuan Gu^b ; ^{gukaixuan@mail.ipc.ac.cn} ; Bo Gao^a ; Guhui Gao^a ; R.D.K. Misra^c ; Bingzhe Bai^a
• 关键词：Deep cryogenic treatment ; Bainite ; Microstructure ; Properties
• 刊名：Materials Science and Engineering: A
• 出版年：2017
• 出版时间：27 January 2017
• 年：2017
• 卷：684
• 期：Complete
• 页码：559-566
• 全文大小：2184 K
• 卷排序：684

文摘

The bainite/martensite (B/M) multiphase microstructure was studied in 0.22C–2.0Mn–1.0Si–0.8Cr–0.8(Mo+Ni) (wt%) bainitic steel subjected to deep cryogenic treatment (DCT) to elucidate the positive effect of DCT on structure and mechanical properties. The study indicates that DCT can improve mechanical properties and wear resistance. It reduces the content of blocky martensite/austenite (M/A) constituents by eliminating unstable retained austenite (RA). At the same time, RA is relatively more enriched in carbon after DCT, compared to the tempering process. During DCT, the brittle martensite is also avoided, since the enhanced recovery reduces the carbon concentration during tempering. Meanwhile, the contraction of unit cell at low temperature promotes the precipitation of fine dispersed carbides and contributes to wear resistance.