文摘
Super austenitic stainless steel was hot-deformed at 1173-1423 K and 0.001-10 s− 1 using a thermo-mechanical simulator Hot deformation parameters were modeled using Arrhenius equation and Zener–Hollomon parameter (Z) Peak, critical (for DRX), maximum flow softening and steady-state stresses vary linearly with ln(Z/A) Processing map was constructed and microstructures at different processing domains were characterized Optimum processing domain was identified as 1300-1350 K and 0.01-0.1 s− 1