Influence of adding nanoparticles on the hardness, tear strength, and permanent deformation of facial silicone subjected to accelerated aging

详细信息    查看全文

• 作者：Adhara S. Nobrega ; DDS^a ; Agda M. Andreotti ; DDS^b ; Amá ; lia Moreno ; DDS^c ; Má ; rio A.C. Sinhoreti ; DDS^d ; Daniela M. dos Santos ; DDS^e ; Marcelo C. Goiato ; DDS^f ; ^{goiato@foa.unesp.br" class="auth_mail" title="E-mail the corresponding author}
• 刊名：The Journal of Prosthetic Dentistry
• 出版年：2016
• 出版时间：October 2016
• 年：2016
• 卷：116
• 期：4
• 页码：623-629.e1
• 全文大小：1363 K

文摘

The efficiency of adding nanoparticles to silicone protection has proven to prevent color degradation. However, reports of other physical property changes in facial silicone are scarce.

Purpose

The purpose of this in vitro study was to evaluate the influence of adding nanoparticles on the hardness, tear strength, and permanent deformation of a facial silicone.

Material and methods

Specimens were made for each test, with 140 for the hardness test, 140 for the permanent deformation test, but 280 for the rupture test. This higher number was due to the fact that the first 140 specimens were ruptured and unusable after the initial reading. ZnO, BaSO₄, and TiO₂ nanoparticles at concentrations of 1% and 2% of silicone were used, as well as specimens without nanoparticles that consisted of only oil paint and of only silicone. Outcomes were measured before and after 1008 hours of accelerated aging. Data were analyzed by nested analysis of variance (ANOVA) and Tukey honest significant differences test (α=.05).

Results

Results showed that the presence of nanoparticles influenced the properties of the assessed groups. The nanoparticles decreased hardness values. The highest values of tear strength were observed for the groups with addition of BaSO₄. The 1% ZnO group without oil paint showed the lowest values of permanent deformation.

Conclusions

Based on the findings of this in vitro study, the use of ZnO nanoparticles is recommended, since they did not negatively affect the properties of the materials evaluated.