The laser melting deposition could realize the form restoration of groove defect.
Tensile strength and elongation could reach relatively 1100 MPa and 10%.
Relative density of LMD repaired zone could reach 99%.
Element content difference of LMD repaired zone is less than ±0.15%.
Microhardness of repaired zone is evenly distributed at 370–390 HV500.