文摘
Multiferroic properties of LaFeO3–PbTiO3 (LFPTO) epitaxial thin films grown on Nb-doped SrTiO3 (0 0 1) (NSTO) substrate by hydrothermal method were investigated at room temperature, which was demonstrated by the ferroelectric (2Pr=3.95 μC/cm2, 2Ec=38.6 kV/cm at applied electric field 66.8 kV/cm) and magnetic (2Mr=12.13 emu/cm3, 2Hc=3000 Oe at applied magnetic field 1.6 T) hysteresis loops. Furthermore, stable multilevel bipolar resistive switching behaviors controlled by the applied reset voltage were observed in the Pt/LFPTO/NSTO/Pt structures. Multiferroic LaFeO3–PbTiO3 thin films combing good resistive switching behaviors have potential application in multifunctional devices.