Influence of tool pin design on properties of dissimilar copper to aluminum friction stir welding

详细信息    查看全文

• 作者：Kush P. MEHTA ; ^{kush_2312@yahoo.com} ; Vishvesh J. BADHEKA ^{vishvesh79@gmail.com}
• 关键词：Cu&ndash ; Al joint ; dissimilar friction stir welding ; pin profiles ; properties ; intermetallic
• 刊名：Transactions of Nonferrous Metals Society of China
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：27
• 期：1
• 页码：36-54
• 全文大小：12939 K
• 卷排序：27

文摘

Dissimilar friction stir welding (FSW) of copper and aluminum was investigated by nine different tool designs, while the rest of the process parameters were kept constant. Mechanical and metallurgical tests such as macrostructure, microstructure, tensile test, hardness, scanning electron microscope and electron X-ray spectrographs were performed to assess the properties of dissimilar joints. The results exhibited that, the maximum joint strength was achieved by the tool of cylindrical pin profile having 8 mm pin diameter. Besides, the fragmental defects increased as the number of polygonal edges decreased, hence the polygonal pin profiles were unsuitable for dissimilar FSW butt joints. Furthermore, the tensile strength increased as the number of polygonal edges increased. Stir zone of polygonal pin profiles was hard and brittle relative to cylindrical tool pin profiles for same shoulder surface. Maximum hardness of HV 283 was obtained at weld made by the polygonal square pin profile. The hard and brittle intermetallic compounds (IMCs) were prominently presented in the stir zone. Phases of IMCs such as CuAl, CuAl2, Cu3Al and Cu9Al4 were presented in the stir zone of dissimilar Cu–Al joints.