文摘
Ordered mesoporous carbon-silica composite was ¡°in situ?transformed into hierarchically porous zeolites ZSM-5 (H-ZSM-5) under water vapor, which synthesized from evaporation induced ¡°tri-constituent?co-assembly of resin, silica and surfactant. The vapor assisted transformation was realized within 2-D hexagonally mesochannels of carbon-silica composite infused with tetrapropylammonium hydroxide at 130 ¡ãC for 72 h. The calcined H-ZSM-5-570 possesses a mesostructure with mean pore sizes of 0.6 and 9.0 nm, BET surface area of 409 cm2/g, and pore volume of 0.54 cm3/g. High-resolution TEM images of H-ZSM-5-570 display that mesoporous walls consisted of zeolite nanocrystals of about 6 nm in the same domain. Weak acidity of H-ZSM-5-570 has also been concluded from ammonia desorption measurements.