Stable, microfabricated thin layer chromatography plates without volume distortion on patterned, carbon and Al2O3-primed carbon nanotube forests
详细信息 查看全文
- 作者：David S. Jensen ; Supriya S. Kanyal ; Vipul Gupta ; Michael A. Vail ; Andrew E. Dadson ; Mark Engelhard ; Richard Vanfleet ; Robert C. Davis ; Matthew R. Linford
- 关键词：Atomic layer deposition ; Thin layer chromatography ; CVD of carbon ; Template carbon nanotubes ; Carbon nanotubes
- 刊名：Journal of Chromatography A
- 出版年：2012
- 出版时间：28 September, 2012
- 年：2012
- 卷：1257
- 期：Complete
- 页码：195-203
- 全文大小：1407 K
文摘
Some of us recently described the fabrication of thin layer chromatography (TLC) plates from patterned carbon nanotube (CNT) forests via direct infiltration/coating of the CNTs by low pressure chemical vapor deposition (LPCVD) of silicon from SiH4, followed by high temperature oxidation of the CNTs and Si. Herein we present an improved microfabrication process for the preparation of these TLC plates. First, a few nanometers of carbon and/or a thin film of Al2O3 is deposited on the CNTs. This method of priming the CNTs for subsequent depositions appears to be new. X-ray photoelectron spectroscopy confirms the presence of additional oxygen after carbon deposition. After priming, the plates are coated by rapid, conformal deposition of an inorganic material that does not require subsequent oxidation, i.e., by a fast pseudo atomic layer deposition (¦×-ALD) of SiO2 from trimethylaluminum and tris(tert-butoxy)silanol. Unlike devices described previously, faithful reproduction of the features in the masks is still observed after oxidation. A bonded, amino phase on the resulting plates shows fast, highly efficient separations of fluorescent dyes (plate heights in the range of 1.6-7.7 ¦Ìm). Extensive characterization of the new materials by TEM, SEM, EDAX, DRIFT, and XPS is reported. A substantially lower process temperature for the removal of the CNT scaffold is possible as a result of the already oxidized materials used.