The effect of single overloads in tension and compression on the fatigue crack propagation behaviour of short cracks

详细信息    查看全文

• 作者：Xiang Zhou^a ; ^b ; ; Hans-Peter Gaenser^a ; Reinhard Pippan^b ; ^c
• 关键词：Overload ; Crack closure ; Residual stress ; Threshold of stress intensity ; Effective threshold
• 刊名：International Journal of Fatigue
• 出版年：2016
• 出版时间：August 2016
• 年：2016
• 卷：89
• 期：Complete
• 页码：77-86
• 全文大小：3481 K

文摘

The crack propagation behaviour in cast quenched and tempered steel after one overload cycle in tension as well as in compression on short cracks is investigated in deep notched specimens. The overload cycle exhibits a significant influence on the fatigue life endurance, due to the formation of an overload plastic zones in front of the crack tip. The crack propagation after overload cycles is investigated by inspection of the fatigue threshold R-curve and fatigue crack propagation rate. Tension overload increased the long crack threshold and reduced the R-curve effect, whereas overloads in compression reduced the crack growth resistance and shifted the threshold value to larger crack extension. A simple FE simulation was also performed to investigate the variation in the contribution of plasticity induced crack closure during crack propagation after the overload. Macroscopic mechanistic and dislocation models are introduced to explain the results obtained.