A cold rolling reduction of 65% produced a large yield strength of 1442 MPa.
1273 K annealing for 1 h on cold-worked material led to recrystallization to a micron-scale equi-axed grain structure.
Recrystallization changed the chemistry and volume fractions of the B2 and f.c.c. phases.
The recrystallized material shows a good room temperature yield strength (600 MPa).