- 作者：Farzana Ansari ; Jennifer Chang ; James Huddleston III ; Douglas Van Citters ; Michael Ries ; Lisa Pruitt
- 关键词：Crosslinked UHMWPE ; Tibial post fracture ; Failure analysis ; Oxidation
- 刊名：The Knee
- 出版年：December, 2013
- 年：2013
- 卷：20
- 期：6
- 页码：609-613
- 全文大小：1008 K
Background
Highly crosslinked ultra-high molecular weight polyethylene (UHMWPE) has shown success in reducing wear in hip arthroplasty but there remains skepticism about its use in Total Knee Replacement (TKR) inserts that are known to experience fatigue loading and higher local cyclic contact stresses.Methods
Two Legacy Posterior-Stabilized (LPS) Zimmer NexGen tibial implants sterilized by gamma irradiation in an inert environment with posts that fractured in vivo were analyzed. Failure mechanisms were determined using optical and scanning electron microscopy along with oxidative analysis via Fourier Transform Infra-Red (FTIR) spectroscopy.
Results
Micrographs of one retrieval revealed fatigue crack initiation on opposite sides of the post and quasi-brittle micromechanisms of crack propagation. FTIR of this retrieval revealed no oxidation. The fracture surface image of the second retrieval indicated a brittle fracture process and FTIR revealed oxidation in the explant.
Conclusions
These two cases suggest that crosslinking of UHMWPE as a manufacturing process or sterilization method in conjunction with designs that incorporate high stress concentrations, such as the tibial post, may reduce material strength. Moreover, free radicals generated from ionizing radiation can render the polymer susceptible to oxidative embrittlement.
Clinical relevance
Our findings suggest that tibial post fractures may be the results of in vivo oxidation and low level crosslinking. These and previous reports of fractured crosslinked UHMWPE devices implores caution when used with high stress concentrations, particularly when considering the potential for in vivo oxidation in TKR.