As-milled Fe–Si–Al powders were annealed at various temperature.
The change of morphology and microstructure of as-annealed Fe–Si–Al was examined.
Complex permittivity decrease significantly after annealed over 400 °C and permeability increase as annealing temperature rises.
The precipitation process in annealing and its effect on permittivity were analyzed.