The MnAl ε → τ phase transition studied by in situ synchrotron X-ray diffraction.
A cooling rate of 10 °C/min yields pure τ-phase when cooled from high temperature.
No intermediate ε’-phase was observed during the ε-τ-phase transition process.
C doping stabilizes the τ-phase whereas B doping destabilises the τ-phase.