Five-period GaAsN/GaAs multiple quantum wells grown by varying nitrogen pressure. Low interface roughness because of nitrogen’s occupancy at arsenic lattice sites. A relatively sharp interface-induced high intensity in photoluminescence spectra. 100-fold improvement in optical properties after rapid thermal annealing at 700 °C.