The amount of Cu coating by chemical plating was investigated based on quadratic regression orthogonal experimental design being adapted to the variation law of temperature, pH value and Ni2+ concentration, and the relevant regression equation was expressed as y=2.1609+0.5295×10−3T2-0.0342P2-0.0265N2+0.0023TP+0.0020TH+0.0199PN-0.0959T+0.3814P-0.2073N. The results showed that the deposition rate augmented with the increasing in temperature, pH value and Ni2+ concentration. The experimental parameters of the optimal coating were temperature 75 °C, pH value 8.5 and Ni2+ concentration 1.2 g/L. The electrochemical tests indicated that the cycle stability increased from 60.66 % to 75.58 % , indicating that the treated alloy exhibited better corrosion resistance.