Microstructure and hot deformation behavior of AlMg6 alloy produced by equal-channel angular pressing

详细信息    查看全文

• 作者：Gholamreza Khalaj ; Mohammad Javad Khalaj ; Ali Nazari ; ^{alinazari84@aut.ac.ir}
• 关键词：Hot deformation ; ECAP ; Dynamic recrystallization ; AlMg6 alloy
• 刊名：Materials Science and Engineering: A
• 出版年：2012
• 出版时间：30 April, 2012
• 年：2012
• 卷：542
• 期：Complete
• 页码：15-20
• 全文大小：2202 K

文摘

Experimental work carried out to assess the strain rate and temperature affected deformation behavior of equal-channel angular pressed AlMg6 alloy. Elevated temperature compression test performed at temperatures ranged from 360 to 520 ¡ãC, four strain rates of 0.001, 0.01, 0.1 and 1 s^?. The flow stress curves displayed two kinds of different behaviors, which, at low temperatures or high strain rates, during the initial stage of deformation there is an increase in the flow stress, whereas, at high temperatures or low strain rates, flow curve decreases continuously from yield point due to occurrence of dynamic recrystallization phenomena. Activation energy of deformation is calculated as 185.5 KJ mol^? for the alloy. Steady state strain rate sensitivity parameters were calculated for the strain rate ratios of (1/10), (10/100). The increasing of the m values from 0.1 to 0.4 for the applied strain rate ratios of (10/100) and (1/10), respectively, is assumed to be the result of changing the deformation mechanism from recovery to recrystallization. The effects of number of passes and strain path have been studied on the mechanical and microstructural characteristics of this alloy.