Effect of magnesium ion incorporation on the thermal stability, dissolution behavior and bioactivity in Bioglass-derived glasses

详细信息    查看全文

• 作者：Marina T. Souza ; Murilo C. Crovace ; Cornelia Schr枚der ; Hellmut Eckert ; Oscar Peitl ; Edgar D. Zanotto
• 关键词：Bioactive glass ; Bioactivity ; Crystallization ; Nuclear magnetic resonance
• 刊名：Journal of Non-Crystalline Solids
• 出版年：15 December, 2013
• 年：2013
• 卷：382
• 期：Complete
• 页码：57-65
• 全文大小：1445 K

文摘

There is a strong discrepancy in the literature regarding the effect of magnesium on bioactive glasses. Hence the present study is focused on the physical and chemical behavior of the 鈥済olden standard鈥?45S5 glass and magnesium-containing bioactive glasses developed here to evaluate their reactivity and in vitro bioactivity. The aim of this study was to analyze the influence of CaO replacement by MgO, especially its effect on the rate of formation of the apatite-like layer at the glass surface, the reaction kinetics between the glasses and simulated body fluid (SBF-K9) and on the glass stability against devitrification during heating. Five melt-derived bioactive glasses of the system 24.3Na₂O-26.9(xCaO 鈭?#xA0;(1 鈭?#xA0;x)MgO)-46.3SiO₂-2.5P₂O₅ (x = 1; 0.875; 0.75; 0.625 and 0.5) were synthesized with CaO progressively replaced by MgO. Their thermal stability on heating was characterized by DSC analysis. Their degradation and ability to form an apatite-like layer were evaluated through in vitro tests by immersion in SBF-K9; FTIR, ion selective electrode analysis and by solid state nuclear magnetic resonance (NMR) spectroscopy. Our results indicate that magnesium plays an important role in the stability of this glass family, defined as the difference between the glass transition temperature T_g and crystallization temperature T_x. The lower T_g observed in the MgO-rich glasses and insignificantly changed solubilities, as well as the ²⁹Si NMR results suggest that in this glass system MgO does not act as a network intermediate or former oxide, but as network modifier, as we expected. Dissolution kinetics, FTIR, and solid state ³¹P and ¹H MAS-NMR consistently indicate that partial replacement of CaO by MgO in the bioglass does not influence the rate at which the initial amorphous calcium phosphate (ACP) layer is precipitated when the glass is exposed to SBF. In contrast it greatly reduces the rate of conversion of this precursor phase to the crystalline hydroxycarbonate apatite (HCA)-layer.