Ultrasonic impact treatment produces a gradient nano-to-micron-grained structure in the surface layer of CP titanium. Dislocation glide, twinning and shear banding mechanisms are at work at different depths below the surface under tension. Shear bands in hardened surface layer develop alternatively in conjugate directions of maximum tangential stresses. Shear band evolution and self-organization are analyzed using the energy balance approach.