Microstructures changed from hypoeutectic to hypereutectic with scanning speed.
Volume fraction of martensite increased with scanning speed.
Wear resistance of the optimized layer was increased by 29.76 times.
Oxide films formed on the alloyed surface of the layers substantially enhanced the wear resistance.
Microstructure affected the crack or fracture behavior of the matrix on loading.