Ceramic macroporous reticular alumina foams with a pore size of 15, 20 and 25 pores per inch (ppi) were prepared by the Schwartzwalder method and sintered at 1200 °C to preserve a high porosity. TiO2 thick films were supported on the foam surface by a wash coating process, using Degussa P25 as a TiO2 nanopowder source. After annealing at 600 °C, films with an adequate adhesion and with a thickness of 5–10 μm were obtained. An increasing pore size of the supported foams improves the specific photocatalytic activity of the TiO2 coated scaffolds, the flow of solution through the highly active porous foam structure and the better access of light to the active TiO2 surface.