GZO film deposited on 180 °C glass in open air by atmospheric pressure plasma jet. Multiple depositions significantly enhance deposition rate and film properties. The resistivity (9.4 × 10−4 Ω cm) improved by 33%. The deposition rate (110 nm/min) improved by 35%.