Oxidation protection of Ti-6Al-4V alloy using a novel glass-amorphous silica composite coating

详细信息    查看全文

• 作者：Zunqi Xiao ; Fatang Tan ; Wei Wang ; Fazhe Sun ; Hongfei Lu ; Xiaolin Qiu ; Jianguo Chen ; Xueliang Qiao
• 关键词：D. Glass ; Ti&ndash ; 6Al&ndash ; 4V alloy ; Amorphous silica ; Composite coating
• 刊名：Ceramics International
• 出版年：March, 2014
• 年：2014
• 卷：40
• 期：2
• 页码：3503-3509
• 全文大小：2906 K

文摘

A novel glass-amorphous silica composite coating was prepared by the slurry method in order to improve the oxidation resistance of Ti-6Al-4V alloy at high temperatures. The microstructure of the as-prepared composite coating was analyzed by SEM, XRD and EDS techniques. The oxidation resistance and the microstructure evolution of the composite coating at 800 掳C for 50 h were also studied. The results show that mass gains of the specimens coated with the composite coating were far less than that of the uncoated ones after oxidation of 50 h. Thick oxide scales composed of plate-like rutile TiO₂ and some granular 伪-Al₂O₃ formed on bare Ti-6Al-4V alloy, while quartz, cristobalite and diopside were observed in the composite coating, which are useful crystals for slowing the inward diffusion of oxygen to the substrate. The cross-sectional EDS line scanning images show that inward diffusion of oxygen and outward diffusion of Ti through the composite coating were insignificant. The microhardness profile reveals that the solid solution oxygen in Ti-6Al-4V alloy with composite coating was limited.