An extensive study of hydrogen-induced cracking susceptibility in an API X60 sour service pipeline steel
详细信息 查看全文
- 作者：M.A. Mohtadi-Bonaba ; c ; m.mohtadi@usask.ca" class="auth_mail" title="E-mail the corresponding author ; M. Eskandarib ; c ; K.M.M. Rahmanc ; R. Ouelletc ; J.A. Szpunarc
- 关键词：Hydrogen-induced cracking ; Electron backscatter diffraction ; Hydrogen-charging ; Fracture surface ; Crack propagation
- 刊名：International Journal of Hydrogen Energy
- 出版年：2016
- 出版时间：23 February 2016
- 年：2016
- 卷：41
- 期：7
- 页码：4185-4197
- 全文大小：4048 K
文摘
- •
HIC susceptibility under external stress in X60SS pipeline steel was investigated.
- •
Hydrogen trapping behavior in X60SS pipeline steel was studied.
- •
SEM observations showed that HIC cracks were propagated in different directions.
- •
Effect of different microstructural parameters on hydrogen cracking was discussed.