High amount hydrogen loading into Pd by all solid-state electrolysis was performed.
Hydrogen-induced super-abundant-vacancies form due to high hydrogen potential.
Phase separation into different vacancy concentration phases was observed.
Vacancy-containing Pd-hydrides change phases depending on hydrogen potential.
Sub-micron voids form as a result of a phase transition.