Fatigue of NiTi drops to 104 cycles before reaching martensitic transformation. Early crack nucleation and fast crack growth occurs in NiTi even at low strains. R-phase improves the low cycle fatigue of NiTi as it acts as a stress reliever. Martensitic transformation is triggered at the crack advancing in superelastic NiTi. Transformation strains provide additional driving force for crack opening.