Interface characteristics and fracture behavior of brazed polycrystalline CBN grains using Cu-Sn-Ti alloy

详细信息    查看全文

• 作者：Wen-Feng Ding ; Jiu-Hua Xu ; Zhen-Zhen Chen ; Qing Miao ; Chang-Yong Yang
• 关键词：Brazing ; Fracture ; Interfaces ; Polycrystalline CBN grain
• 刊名：Materials Science and Engineering: A
• 出版年：2013
• 出版时间：1 January, 2013
• 年：2013
• 卷：559
• 期：Complete
• 页码：629-634
• 全文大小：972 K

文摘

Polycrystalline CBN grains were brazed onto AISI 1045 steel matrix using Cu-Sn-Ti brazing alloy. Brazing temperature was 880 ¡ãC, 900 ¡ãC, 920 ¡ãC respectively, and the holding time was 8 min. Interface characteristics, elemental distribution and fracture behavior were analyzed in detail by means of scanning electron microscopy, energy dispersive spectroscopy and testing machine for grain compressive strength. The maximum value of the mean compressive strength of brazed PCBN grains reached 879.3 MPa when the brazing temperature was 900 ¡ãC. The resultants layer composed of TiN, TiB₂, TiB and TiAl₃ was formed at grain/alloy interface. Elemental distribution showed that Ti mainly concentrated within the interface zone. The intercrystalline fracture along the CBN/CBN particle boundary was the main fracture modes of brazed polycrystalline CBN grains.