Al-50Si alloys were joined by ultrasound-induced TLP at only 390 °C in air.
Molten metal was observed under the arc shape oxide.
Bonding time was substantially shortened by U-TLP bonding.
A stage of isothermal solidification existed.
The shear strength of composite joints could reach ∼94.2 MPa.