Al-rich portion of Al–Fe binary phase diagram was experimentally determined.
The α/ε phase equilibrium composition at 1150 °C was determined by DC method.
Solubility ranges of ζ, η and θ phases expand to Fe side with increasing temperature.
Invariant reaction among L, η and θ phases is peritectic.