Wheat-gluten/montmorillonite clay multilayer-coated paperboards with high barrier properties

详细信息    查看全文

• 作者：Hasan T眉re ; Mikael G盲llstedt ; Eva Johansson ; Mikael S. Hedenqvist
• 关键词：Wheat gluten ; Montmorillonite ; Paperboard ; Multilayer coating ; Barrier properties
• 刊名：Industrial Crops and Products
• 出版年：November, 2013
• 年：2013
• 卷：51
• 期：Complete
• 页码：1-6
• 全文大小：1263 K

文摘

This study presents the oxygen-barrier properties of paperboards with a wheat gluten (WG)/montmorillonite clay (MMT) multilayer coating, in which MMT was sandwiched between two layers of WG. Urea was added to the WG to facilitate the coating procedure and the clay was applied as an aqueous dispersion. With a coating thickness of 鈭?0 渭m, oxygen transmission rates were 8-10 cm³/(m² day atm) at 50% RH, which meant that the oxygen barrier was ca. 25 times better than that given by a single-layer WG-coated paperboard (uncoated paperboard showed infinite values). The water vapor transmission rate (WVTR) was 28-39 g/(m² day) using a 50-0% RH gradient, which was 6- to 8-fold lower than the value for uncoated paperboard. Tensile tests revealed small, if any, mechanical effects when the paperboard was coated. A protein solubility analysis indicated that urea-containing WG films were slightly more intermolecularly cross-linked than urea-free WG films. X-ray diffraction revealed that the MMT layer consisted of unswollen tactoids similar to those observed in the MMT powder. The Cobb₆₀ data showed that both WG and clay increased the water absorbency.