TiC-316L stainless steel cermets have been prepared by melt-infiltration.
Fine-grained cermets show lower wear rates than coarse-TiC equivalents.
The cermets show a transition from two- to three-body abrasive wear.
Adhesive wear is also observed, with a high O content tribolayer formed.
Focused ion beam microscopy reveals sub-surface damage mechanisms.